Hi Siliang: The first thing is that you have misidentified the edge position. Itis way too high in all the data sets. Put it at the inflection point of the main rise in the absorption curve and you will find that the problem is much reduced. The second thing is that you have a very bad backgrund problem in your data and, in my estimation your usable data range is no moe than k=2 to k=8. In fact, my suggestion is that you truncate the data by setting the spline range to end at 8. The FT range should probably be set at 2-8 or even 2-7 (somewhere in that range and put a window sill of dk=2 to get rid of some of the ringing. Once you do those things the data will look much more reasonable. These data could probably have used some longer counting times. Where did you take the data? Carlo On Mon, 8 Aug 2016, Siliang Chang wrote:
Dear all,
I am new to XAFS data analysis. I?m currently working on the XAFS data of atomic layer deposited mixed oxide thin film: SnTiOx. I have both Sn and Ti K edge data, and was able to fit Sn edge using a model of (Sn,Ti)O2 solid solution. However, Ti data really confuses me (please see attached file). With Rbkg set to 1, there is a doublet in 1-2 Å region in every data, this is something I have never seen in the literature. I?m wondering if this is normal? Does this mean I should set a larger Rbkg value, say, around 1.5?
I?ve tried to fit the abovementioned Ti data using several models: anatase, rutile, (Sn,Ti)O2 solid solution, perovskite (N is fixed at 6 for all of those), so far no success. I would really appreciate if you can comment on my data processing, any suggestions are welcomed, as I?m new to this, I?m not sure if I?m doing it the right way.
Thank you very much.
Best regards,
Siliang Chang
-- Carlo U. Segre -- Duchossois Leadership Professor of Physics Interim Chair, Department of Chemistry Director, Center for Synchrotron Radiation Research and Instrumentation Illinois Institute of Technology Voice: 312.567.3498 Fax: 312.567.3494 segre@iit.edu http://phys.iit.edu/~segre segre@debian.org