27 Jun
2013
27 Jun
'13
1:48 p.m.
Hello All, If I have a Ta(1-x)Ge(x)O(y) thin film, with Germanium concentration of a few percent, is it possible in principle to get useable fluorescence-mode EXAFS spectra around the Ge K edge (11.1 keV)? Or is it likely that the spectra would be complicated by additional Ge fluorescence excited by processes triggered by Tantalum L edge absorption (9.88, 11.13, 11.68 keV)? Thanks, Darren