<div dir="ltr"><p class="MsoNormal"><span lang="EN-US">Dear All,<span></span></span></p><p class="MsoNormal"><span lang="EN-US"><br></span></p>

<p class="MsoNormal"><span lang="EN-US">I have been trying to fit EXAFS signal of YbVO4 both in bulk and nanoparticles form. Here, I would like to estimate so2 from bulk (reference) and subsequently use
the number, as normalization parameter, to calculate the co-ordination number in all nanoparticles. Nanoparticles were synthesized by solution route. From
our earlier understanding on the synthesis, in some cases, Yb may or may not completely involve in reaction. Therefore, I except Yb in two environments, one surrounded by mere
oxygen (in precise oxygen-Hydrogen; due to disorder one may expect a single peak)
and another one in YbVO4 environment. With this info and for reasonable fit, I have
used two so2 as free parameters for N: one for first shell (oxygen at two distances) and another for
rest other shells.  If I use single so2, I
obtain the value of around 0.92 with unsatisfactory fit whereas the fit seems plausible with two so2 i.e., 0.75 and 2.2, respectively. Using the same
strategy, I could successfully fit the nanoparticles again with large second
so2 (1.79). From literature and IFEFFIT earlier discussion, i understood that so2 should be between 0.8-1.2 value. Here, </span>I would like to know, does this huge second so2 value makes sense? is the obtained so2 value can be used to calculated coordination number for unknown? Further, i have attached my worked files with this message.</p><p class="MsoNormal"><br></p><p class="MsoNormal">Regards,</p><p class="MsoNormal">Raj</p></div>