Hi all,<br><br>I am looking at EXAFS of thin film metal oxides.  I am varying both metal content and the oxygen content of the films. I aligned the scans with a metal reference foil collected simultaneously.  In Artemis, I have noticed that when changing between films with no extra oxygen versus those with extra oxygen there is a shift in the fitted E0 of ~1.5 eV (after aligning to the foil). I tried setting the E0 in Athena to the peak of the 1st derivative and the peak of the white line with the same result (~7 eV difference). I was a little surprised by the offset because in Athena the E0 values varied by <0.5 eV. I am not sure if the argument could be made that this shift is a result in a changing oxidation state because it doesn't show up in the XANES (at least qualitatively).  Are there other experimental effects that could cause a shift like this, or is this likely something real in my material? If anyone want to see a representative group of data, let me know.<br>
<br>I also have an unrelated quick (I think) question on the EXAFS equation. In some references I see a term 1/(k R)^2 and in others it is 1/(k R^2). I couldn't really see any reason for the difference, unless it is to correct for subtle differences in how the other terms are defined.<br>
<br>Thanks<br>Brandon<br>