Hi<BR>
I saw your figure. The second peak of Nanocrystal in wurtzite generally is week or not, because there is an amount of disorder in second shell.<BR>
The second peak in your fitting may make a problem.  <BR>
First, Fit your data in first shell with 4 nitrogen atoms, not with second shell. After that, you can fit second shell with 'set first shell varables'.<BR>
To fit second shell is not easy. when you fit second shell, check the number of second shell atoms. I think there are not 12 In around probe atom.<BR>
<BR><BR> <BR>

<HR id=stopSpelling>
<BR>
Date: Mon, 12 Jan 2009 15:30:52 +0700<BR>From: kaswat@gmail.com<BR>To: ifeffit@millenia.cars.aps.anl.gov<BR>Subject: Re: [Ifeffit] How to keep enot, delr, and ss within acceptable limits<BR><BR><BR>
<DIV>Dear all,</DIV>
<DIV> </DIV>
<DIV>I have the same problem with Hashem. </DIV>
<DIV> </DIV>
<DIV>My sample is nanocrystal Wurtzite InN (XRD and AFM results). I do the absorption experiment at In L3-edge at room temperature. After an data processing process, I get 2 broad peaks in FT. When i try to fitting a Wurtzite InN model to the EXAFS spectra for the first and second shells, I always get unacceptable parameters. First of all, I try to change my WZ InN model (changing lattice constant a and c, u-parameter) but it is inefficiently. How could I do?</DIV>
<DIV> </DIV>
<DIV>This figure 1 shown a FT of In-L3 EXAFS spectra, the Blue line is my 2 broad peaks and red line is calculate with my WZ InN model which set all parameter to initial value (not guess any thing).</DIV>
<DIV> </DIV>
<DIV>figure 1 >> <A href="http://nanotech.sytes.net/kaswat/01.emf">http://nanotech.sytes.net/kaswat/01.emf</A></DIV>
<DIV> </DIV>
<DIV>After I have read Bruce's mail ("If your sigma^2 parameter is negative, perhaps you have too much structural disorder in your model and the fit is compensating by inflating those paths with a negative sigma^2."). How do I construct a WZ InN model which have too many structural disorder.</DIV>
<DIV> </DIV>
<DIV>P.S. I have read some papers, they have use model of nanocrystalline alloy which containing amorphous model. How to construct an amorphous model like they.</DIV><BR clear=all><BR>-- <BR>Mr. Kittiphong Amnuyswat [kaswat]<BR><BR>Post Graduate student <BR>College of KMITL Nanotechnology<BR><BR>Contact : <A href="mailto:kaswat@gmail.com">kaswat@gmail.com</A>, <A href="mailto:nakz_zz@hotmail.com">nakz_zz@hotmail.com</A> [MSN Available]<BR><br /><hr />클릭 한번으로 전세계 이미지가 검색됩니다.  <a href='http://www.live.com/?scope=images' target='_new'>지금 라이브 검색을 체험해보세요.</a></body>