<div>I have the same problem with Hashem. </div>
<div> </div>
<div>My sample is nanocrystal Wurtzite InN (XRD and AFM results). I do the absorption experiment at In L3-edge at room temperature. After an data processing process, I get 2 broad peaks in FT. When i try to fitting a Wurtzite InN model to the EXAFS spectra for the first and second shells, I always get unacceptable parameters. First of all, I try to change my WZ InN model (changing lattice constant a and c, u-parameter) but it is inefficiently. How could I do?</div>

<div> </div>
<div>This figure 1 shown a FT of In-L3 EXAFS spectra, the Blue line is my 2 broad peaks and red line is calculate with my WZ InN model which set all parameter to initial value (not guess any thing).</div>
<div> </div>
<div>figure 1 >> <a href="http://nanotech.sytes.net/kaswat/01.emf">http://nanotech.sytes.net/kaswat/01.emf</a></div>
<div> </div>
<div>After I have read Bruce's mail ("If your sigma^2 parameter is negative, perhaps you have too much structural disorder in your model and the fit is compensating by inflating those paths with a negative sigma^2."). How do I construct a WZ InN model which have too many structural disorder.</div>

<div> </div>
<div>P.S. I have read some papers, they have use model of nanocrystalline alloy which containing amorphous model. How to construct an amorphous model like they.</div><br clear="all"><br>-- <br>Mr. Kittiphong Amnuyswat [kaswat]<br>
<br>Post Graduate student <br>College of KMITL Nanotechnology<br><br>Contact : <a href="mailto:kaswat@gmail.com">kaswat@gmail.com</a>, <a href="mailto:nakz_zz@hotmail.com">nakz_zz@hotmail.com</a> [MSN Available]<br>